E308LT0-1
AWS A5.22 CLASS E 308LT0-1/-4
E308TL0 is a flux cored wire for single or multi-pass welds on stainless steels. E308TL0 is noted for its low spatter generation, excellent bead shape and appearance and ease of slag removal. It has very good deposit efficiency when used for flat and fillet welds of medium and heavy thickness plates. It has been designed to be used with 100% CO2 or 75-80% Argon + balance CO2 mixed shield gas. The high chromium and nickel content of E308TL0 provides weld deposits with scaling and heat resistance in addition to corrosion resistance.
Applications:
E308TL0 is used extensively in the fabrication of type 308 stainless steel structures, furnace parts, high temperature containers, and aircraft heaters. E308TL1 may be used to weld straight chromium type stainless steels (ie: 12Cr 410) when pre-heat and post-heat treatment is not possible. E308TL0 may also be used to join stainless steels to mild steel and for stainless cladding of mild and low alloy steels.
TYPICAL WELD METAL CHEMISTRY
(% – Tested with 80% Argon+20% CO2 Shield Gas)
C | 0.04 |
Mn | 1.87 |
Si | 0.75 |
Cr | 19.50 |
Ni | 10.30 |
TYPICAL MECHANICAL PROPERTIES OF WELD DEPOSIT
(As welded – tested with 80%Argon + 20% CO2
Shield Gas)
Ultimate tensile strength (psi) | 88,500 min |
Elongation in 2" (%) | 36% |